ASTM A335 is the standard specification for seamless ferritic alloy steel pipe for high temperature service. It covers sever grades: P1, P2, P5, P5b, P5c, P9, P11, P12, P15, P21, P22, P23, P91, P92, P122, out of which P5, P9, P11, P22, P91, and P92 are most widely utilized in practice. The specification covers nominal wall and minimum wall chrome-molybdenum( also known as Cr-Mo, or Cr-Moly) alloy steel pipe intended for high-temperature application. Pipe ordered to this specification shall be suitable for bending, flanging(vanstoning), and similar forming operations, and for fusion welding. ASTM A335 P11, P22, P91 and P92 are commonly used in power plants and chemical-petrochemical industry, while P9 and P5 are mainly used in petroleum refineries. Hebei Metals supplies ASTM A335 Cr-Mo alloy steel seamless pipes sized from 1/2″ to 24″(NPS15 ~ NPS600) ranging in wall thickness from SCH20 to XXS or even thicker.

1. UNS Designations and Chemical Composition

   
   

   ASTM A335/ A335M Chemical Composition %
   Grade	UNS	C	Mn	P	S	Si	Cr	Mo	Others
   P1	K11522	0.10-0.20	0.30-0.80	0.025	0.025	0.10-0.50	-	0.44-0.65	-
   P2	K11547	0.10-0.20	0.30-0.61	0.025	0.025	0.10-0.30	0.50-0.81	0.44-0.65	-
   P5	K41545	0.15	0.30-0.60	0.025	0.025	0.5	4.00-6.00	0.45-0.65	-
   P5b	K51545	0.15	0.30-0.60	0.025	0.025	1.00-2.00	4.00-6.00	0.45-0.65	-
   P5c	K41245	0.12	0.30-0.60	0.025	0.025	0.5	4.00-6.00	0.45-0.65	*A
   P9	S50400	0.15	0.30-0.60	0.025	0.025	0.25-1.00	8.00-10.00	0.90-1.10	-
   P11	K11597	0.05-0.15	0.30-0.60	0.025	0.025	0.50-1.00	1.00-1.50	0.44-0.65	-
   P12	K11562	0.05-0.15	0.30-0.61	25	0.025	≤0.50	0.80-1.25	0.44-0.65	-
   P15	K11578	0.05-0.15	0.30-0.60	0.025	0.025	1.15-1.65	-	0.44-0.65	-
   P21	K31545	0.05-0.15	0.30-0.60	0.025	0.025	0.5	2.65-3.35	0.80-1.06	-
   P22	K21590	0.05-0.15	0.30-0.60	0.025	0.025	0.5	1.90-2.60	0.87-1.13	-
   P23	K41650	0.04-0.10	0.10-0.60	0.03	0.01	0.5	1.90-2.60	0.05-0.30	*B
   P36	K21001	0.10-0.17	0.80-1.20	0.03	0.025	0.25-0.50	0.3	0.25-0.50	*C
   P91	K91560	0.08-0.12	0.30-0.60	0.02	0.01	0.20-0.50	8.00-9.50	0.85-1.05	*D
   P92	K92460	0.07-0.13	0.30-0.60	0.02	0.01	0.5	8.50-9.50	0.30-0.60	*E
   P122	K92930	0.07-0.14	0.7	0.02	0.01	0.5	10.00-11.50	0.25-0.60	*F
   P911	K91061	0.09-0.13	0.30-0.60	0.02	0.01	0.10-0.50	8.50-9.50	0.90-1.10	*G

*The UNS designation is established in accordance with Practice E527, and SAE J 1086 – Practice for numbering metals and alloys.

*All values are the maximum unless a range is furnished.

*A – 4 times of Carbon≤Titanium≤0.70% or Columbium:8 times of Carbon~10 times of Carbon.

*B – V:0.20-0.30, Cb:0.02-0.08, B: 0.0010-0.006, N:≤0.0015, Al:≤0.030, W:1.45-1.75, Ni:≤0.40, Ti: 0.005-0.060, Ti/N:≥3.5.

*C – Ni:1.00-1.30, Cu:0.50-0.80, Cb:0.015-0.045, V:≤0.02, N:≤0.02, Al:≤0.050.

*D – V:0.18-0.25, N:0.030-0.070, Ni:≤0.40, Al:≤0.02, Cb:0.06-0.10, Ti:≤0.01, Zr:≤0.01.

*E – V:0.15-0.25, N:0.03-0.07, Ni:≤0.40, Al:≤0.02, Cb:0.04-0.09, W:1.5-2.0, B:0.001-0.006, Ti:≤0.01, Zr:≤0.01.

*F – V:0.15-0.30, W:1.30-2.50, Cu:0.30-1.70, Cb:0.04-0.10, B:0.0005-0.005, N:0.040-0.1, Ni:≤0.5, Al:≤0.02, (Ti&Zr):≤0.01.

*G – V:0.18-0.25, Ni:≤0.40, Cb:0.060-0.10, B:0.0003-0.006, N:0.04-0.09, Al:≤0.02, W:0.90-1.10, Ti:≤0.01, Zr:≤0.01.

2. Mechanical Properties: Tensile, Yield, Elongation & Hardness

*All values are minimum unless otherwise specified.

*The specimen for elongation test shall be in the gauge length of 2 inches or 50 mm(or 4D).

3. Heat Treatment and Delivery Conditions

ASTM A335 pipes may be either hot finished or cold drawn with finishing treatment listed below:

Pipes of all grades of ASTM A335 except P5c, P23, P91, P92, P122, and P911 shall be reheated, and furnished in the full-annealed, isothermal annealed, or normalized and tempered condition, the minimum tempering temperature  for grades P5, P5b, P9, P21, and P22 shall be 1250°F (675°C), the minimum tempering temperature for grades P1, P2, P11, P12, and P15 shall be 1200°F (650°C). It is recommended that the temperature for tempering should be at least 100°F (50°C) above the intended service temperature; consequently, the purchaser should advise the manufacturer if the service temperature is to be over 1100°F (600°C).

ASTM A335 Pipe of Grades P1, P2, and P12, either hot finished or cold drawn, may be given a final heat treatment at 1200°F (650°C) to 1300°F (705°C) instead of heat treatments above-mentioned.

Pipe of grade P5c shall be given a final heat treatment in the range from 1325°F (715°C) to 1375°F (745°C).

ASTM A335 grades P92 & P911 shall be normalized at 1900°F (1040°C) minimum and tempered at 1350°F (730°C) minimum as a final heat treatment.

Grade P122 shall be normalized at 1900°F (1040°C) minimum, and tempered at 1350°F (730°C) minimum as a final heat treatment.

Grade P23 shall be normalized at 1900°F (1040°C) minimum with air cooling or accelerated cooling and tempered at 1350°F (730°C) minimum as a final heat treatment.

ASTM A335 P91 shall be normalized at 1900°F (1040°C) minimum, and tempered at 1350°F (730°C) minimum as a final heat treatment. Alternatively, liquid quenching and tempering is allowed for thicknesses above 3 inch when mutually agreed upon between the manufacturer and the purchaser. In this case the pipe shall be quenched from 1900°F (1040°C) minimum and tempered at 1350°F (730°C) minimum as final heat treatment.

4. Tests and Examinations

·Unless an alternative nondestructive electric test is selected or otherwise specified by the purchaser, hydrostatic test shall be performed for each length of ASTM A335 pipe.

·Mechanical Tests: pipes of all grades of ASTM A335 shall take transverse or longitudinal tension test and flattening test, hardness test, or bend test. The test will be made on 5% of the pipe from each heat number.

·The nondestructive test (NDT) shall be performed in accordance with Practice E 213, Practice E 309, or Practice E 570. These NDT methods includes: Ultrasonic Examination, which shall be performed to detect both longitudinally and transversely oriented discontinuities; Eddy Current Examination, which has the capability to detect significant discontinuities especially of short abrupt type; Flux Leakage Examination, which is capable of detecting the presence and location of significant longitudinally and transversely oriented discontinuities.

5. How to order an ASTM A335 Pipe

When asking for a quote, it will be very helpful if the client can provide detailed information:

·Name of material: seamless alloy steel pipe.

·Specific grades.

·Manufacture: hot rolled or cold drawn.

·Size: NPS+Schedule Number; O.D+Nominal W.T; O.D+Minimum W.T; I.D+ Nominal W.T; I.D+Minimum W.T.

·Length(fixed or random) and Quantity.

·End Finish(butt welding ends or plain ends).

WORKSHOP EQUIPMENT

PACKAGE DELIVERY 20ft GP:5898mm(Length)x2352mm(Width)x2393mm(High)   24-26CBM

40ft GP:12032mm(Length)x2352mm(Width)x2393mm(High)   54CBM

40ft HC:12032mm(Length)x2352mm(Width)x2698mm(High)    68CBM

In bundle,plastic bags,thin film,wooden pallet,standard seaworthy export packing or as customer demands